LNP ULTEM® SMU5834 Polyetherimide, 20% Carbon Fiber Reinforcement

High modulus with shielding/ conductive characteristics for high-heat applications.

• Features: Electrically Conductive, High Heat Resistance, High Strength
• Forms: Pellets
• Processing Method: Injection Molding

Information provided by LNP, a GE Plastics Company.

This data sheet is labeled Discontinued; however many LNP grades are still active under new names instituted after the SABIC purchase.

物理性能	额定值 (公制)	额定值 (英制)	测试方法
比重	g/cc	g/cc	ASTM D792

机械性能	额定值 (公制)	额定值 (英制)	测试方法
抗张强度(断裂)	MPa	psi	Type I, 5 mm/min; ASTM D638
伸长率 (断裂)			Type I, 5 mm/min; ASTM D638
弯曲强度	MPa	psi	(102 mm Span) 3mm/min; ASTM D790
弯曲模量	GPa	ksi	(102 mm Span) 3mm/min; ASTM D790
悬壁梁缺口冲击强度	J/cm	ft-lb/in	ASTM D256

电气性能	额定值 (公制)	额定值 (英制)	测试方法
表面电阻	ohm	ohm	ASTM D257
静电衰减	<= sec	<= sec	5000V to <50V; FTMS101B

热性能	额定值 (公制)	额定值 (英制)	测试方法
载荷下热变形温度(1.8 MPa)	°C @Thickness 6.35 mm	°F @Thickness 0.250 in	Unannealed; ASTM D648

加工性能	额定值 (公制)	额定值 (英制)	测试方法
料筒后部温度	°C	°F
料筒中部温度	°C	°F
料筒前部温度	°C	°F
射嘴温度	°C	°F
加工（熔体）温度	°C	°F
模具温度	°C	°F
干燥温度	°C	°F
干燥时间	<= hour	<= hour
水分含量			Suggested
背压	MPa	psi
Clamp Pressure	MPa	psi
Shot Size			Suggested
Vent Depth	cm	in
螺杆转速	rpm	rpm