ExxonMobil Escorene™ FL 00212 Ethylene Vinyl Acetate Copolymer (European Grade)

Product Description: FL 00212 is a copolymer of ethylene and vinyl acetate.
Processing Conditions: Processing temperatures above 260°C (500°F) may cause resin degradation. Machines should always be purged with LDPE or suitable cleaning compound before shutdown.

Availability: Africa & Middle East and Europe

Additive:

• Antiblock: No
• Slip: No
• Thermal Stabilizer: Yes

Applications:

• Cast Film
• Co-Extrusion Films
• Compounding
• Freezer Film
• Injection Molding
• Stretch Film

Information provided by ExxonMobil

物理性能	额定值 (公制)	额定值 (英制)	测试方法
密度	g/cc	lb/in³	ExxonMobil method
Vinyl Acetate Content			ExxonMobil method
熔体流动速率	g/10 min @Load 2.16 kg, Temperature 190 °C	g/10 min @Load 4.76 lb, Temperature 374 °F	ASTM D1238

机械性能	额定值 (公制)	额定值 (英制)	测试方法
肖氏硬度 (邵氏 A)	@Time 15.0 sec	@Time 0.00417 hour	Molded Properties; ISO 868
抗张强度(断裂)	>= MPa	>= psi	Molded Properties; ISO 527-2/1A
断裂伸长率，MD			ASTM D882
断裂伸长率，TD			ASTM D882
拉伸模量	GPa	ksi	Molded Properties; ISO 527-2/1
埃尔曼多夫抗撕强度(MD)	g	g	ASTM D1922
埃尔曼多夫抗撕强度(TD)	g	g	ASTM D1922
落锤试验	g	lb	ASTM D1709A
抗张强度(MD : 断裂)	MPa	psi	ASTM D882
抗张强度(TD : 断裂)	MPa	psi	ASTM D882
割线模量(1% 正割 MD)	MPa	psi	ASTM D882
割线模量(1% 正割 TD)	MPa	psi	ASTM D882

热性能	额定值 (公制)	额定值 (英制)	测试方法
熔融温度	<= °C	<= °F	Peak Melting Point; ExxonMobil method
维卡软化温度	°C	°F	ASTM D1525

材料描述		测试方法
Blending Temperature	260