Palm Labs Adhesives TURBO-LOCK SERIES 11-OR Anaerobic Thread Locking Compound

TURBO-LOCK 11-OR SERIES is a fast curing, BLUE, removable, medium strength, oil resistant, primerless, general purpose anaerobic thread-locking compound for bonding and sealing threads. It is highly resistance to heat, vibrations, water, gases, oils, hydrocarbons and many chemicals. Disassembles with hand tools.

Applications:

• Ideal for less active materials such as stainless steel and plated parts.
• Ideal for thread locking plated parts, vibration or moving components.
• Ideal for fasteners between up to ¾” (up to 20 mm) diameters.
• Locks and seals threaded joints-nuts, screws, and studs with improved oil resistance.

Part Numbers for this data: 11-000-OR, 11-001-OR, 11-010-OR, 11-050-OR, 11-250-OR, 11-1000-OR

Information provided by Palm Laboratories Adhesives

物理性能	额定值 (公制)	额定值 (英制)	测试方法
比重	g/cc	g/cc
布氏粘度	cP	cP	RVT Spindle 3 @ 20 rpm

机械性能	额定值 (公制)	额定值 (英制)	测试方法
剪切强度	>= MPa	>= psi	Steel pins and collars; ISO 10964

热性能	额定值 (公制)	额定值 (英制)	测试方法
线性热膨胀系数	µm/m-°C	µin/in-°F	ASTM D696
比热容	J/g-°C	BTU/lb-°F
导热系数	W/m-K	BTU-in/hr-ft²-°F	ASTM C177
Flash Point	>= °C	>= °F

加工性能	额定值 (公制)	额定值 (英制)	测试方法
固化时间	min	hour	Functional
	min	hour	Full
	min @Temperature -55.0 - 150 °C	hour @Temperature -67.0 - 302 °F	Handling
保质期	Month	Month

材料描述		测试方法
外观	Blue
耐化学性	100% Initial Strength Retained	Ethanol at 22°C, at 500hrs
	100% Initial Strength Retained	Gasoline at 22°C, at 500hrs
	100% Initial Strength Retained	Brake Fluid at 22°C, at 500hrs
	100% Initial Strength Retained	Ethanol at 22°C, at 1000hrs
	100% Initial Strength Retained	Gasoline at 22°C, at 1000hrs
	100% Initial Strength Retained	Brake Fluid at 22°C, at 1000hrs
	80% Initial Strength Retained	Water/Glycol at 87°C, at 1000hrs
	90% Initial Strength Retained	Water/Glycol at 87°C, at 500hrs
	90% Initial Strength Retained	Acetone at 22°C, at 1000hrs
	95% Initial Strength Retained	Motor Oil at 125°C, at 1000hrs
	95% Initial Strength Retained	Motor Oil at 125°C, at 500hrs
	95% Initial Strength Retained	Acetone at 22°C, at 500hrs
组成	Dimethacrylate Ester
Max Screw Size	3/4” / 20 mm
Torque	20 N.m	Breakaway, M10 steel nuts and bolts N.m, ISO 10964
	24 N.m	Breakloose, pre-torqued to 5 N.m, M10 steel nuts and bolts, ISO 10964
	24 N.m	Max Prevail, pre-torqued to 5 N.m, M10 steel nuts and bolts N.m, ISO 10964
	7 N.m	Prevail, M10 steel nuts and bolts N.m, ISO 10964