Applications:
| 物理性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 密度 | g/cc | lb/in³ | ISO 1183/A; ASTM D792 |
| 吸水率 | @Temperature 23.0 °C | @Temperature 73.4 °F | Equilibrium, 50% RH; ISO 62; ASTM D570 |
| @Temperature 23.0 °C, Time 86400 sec | @Temperature 73.4 °F, Time 24.0 hour | ISO 62; ASTM D570 | |
| 线性成型收缩率,Flow | cm/cm | in/in | ISO 294-4; ASTM D955 |
| 熔体流动速率 | g/10 min @Load 1.20 kg, Temperature 300 °C | g/10 min @Load 2.65 lb, Temperature 572 °F | ISO 1133; ASTM D1238 |
| 机械性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 洛氏硬度（M 级） | ASTM D785 | ||
| 洛氏硬度（R 级） | ASTM D785 | ||
| 抗张强度(断裂) | MPa | psi | 50 mm/min; ASTM D638 |
| MPa | psi | ISO 527-2/50 | |
| 抗张强度(屈服) | MPa | psi | 50 mm/min; ASTM D638; ISO 527-2/50 |
| 伸长率 (断裂) | 50 mm/min; ASTM D638; ISO 527-2/50 | ||
| 拉伸模量 | GPa | ksi | ISO 527-2/50 |
| GPa | ksi | 50 mm/min; ASTM D638 | |
| 弯曲强度 | MPa | psi | Method I (3 point load), 2.0 mm/min; ASTM D790 |
| MPa | psi | 2.0 mm/min; ISO 178 | |
| 弯曲模量 | GPa | ksi | 2.0 mm/min; ISO 178 |
| GPa | ksi | Method I (3 point load), 2.0 mm/min; ASTM D790 | |
| 悬壁梁缺口冲击强度 | J/cm @Temperature 23.0 °C | ft-lb/in @Temperature 73.4 °F | ASTM D256 |
| kJ/m² @Temperature 23.0 °C | ft-lb/in² @Temperature 73.4 °F | ISO 180/4A | |
| 悬壁梁无缺口冲击强度 | @Temperature 23.0 °C | @Temperature 73.4 °F | ISO 180; ASTM D256A |
| 拉伸冲击强度 | kJ/m² | ft-lb/in² | ASTM D1822 |
| 落锤总能量 | J | ft-lb | 3.39 m/sec; ASTM D3763 |
| 磨损 | [%] Taber; ASTM D1004 |
| 电气性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 体积电阻率 | ohm-cm | ohm-cm | ASTM D257 |
| 介电常数 | @Frequency 60.0 Hz | @Frequency 60.0 Hz | ASTM D150 |
| @Frequency 1.00e+6 Hz | @Frequency 1.00e+6 Hz | ASTM D150 | |
| 介电强度 | kV/mm | kV/in | ASTM D149 |
| 耗散因数 | @Frequency 50.0 Hz | @Frequency 50.0 Hz | ASTM D150 |
| @Frequency 1.00e+6 Hz | @Frequency 1.00e+6 Hz | ASTM D150 | |
| 相比耐漏电起痕指数(CTI) | V @Thickness 2.00 mm | V @Thickness 0.0787 in | Solution A; IEC 60112 |
| 热性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 线形热膨胀系数 - 流动 | µm/m-°C @Temperature -40.0 - 82.0 °C | µin/in-°F @Temperature -40.0 - 180 °F | ASTM D696 |
| Hot Ball Pressure Test | °C | °F | IEC 60335-1 |
| 载荷下热变形温度(0.46 MPa) | °C | °F | Annealed; ISO 75-2/B; ASTM D648 |
| °C | °F | Unannealed; ISO 75-2/B | |
| 载荷下热变形温度(1.8 MPa) | °C | °F | Unannealed; ASTM D648 |
| °C | °F | Annealed; ISO 75-2/A | |
| °C | °F | Annealed; ASTM D648 | |
| 维卡软化温度 | °C @Load 5.10 kg | °F @Load 11.2 lb | Rate A (50°C/h); ASTM D1525; ISO 360/B50 |
| 可燃性(UL94) | @Thickness 1.59 mm | @Thickness 0.0626 in | |
| @Thickness 3.20 mm | @Thickness 0.126 in | ||
| 极限氧指数 | ISO 4289-2 |
| 光学性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 折射率 | ASTM D542; ISO 489 | ||
| 雾度 | ASTM D1003 | ||
| Transmission, Visible | ASTM D1003 |
| 材料描述 | 测试方法 | |
|---|---|---|
| Average Extent of Burring | 3 cm | ASTM D635 |