| 物理性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 密度 | g/cc | lb/in³ | Average value: 1.38 g/cc Grade Count:81 |
| 吸水率 | Average value: 3.91 % Grade Count:52 | ||
| 平衡吸湿 | Average value: 1.88 % Grade Count:37 | ||
| 饱和吸水率 | Average value: 6.55 % Grade Count:6 | ||
| 处理 | Average value: 0.100 Grade Count:4 | ||
| 线性成型收缩率 | cm/cm | in/in | Average value: 0.00822 cm/cm Grade Count:64 |
| 线性成型收缩率，横向 | cm/cm | in/in | Average value: 0.00895 cm/cm Grade Count:28 |
| 熔体流动速率 | g/10 min | g/10 min | Average value: 43.7 g/10 min Grade Count:21 |
| 机械性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 洛氏硬度（M 级） | Average value: 87.0 Grade Count:5 | ||
| 洛氏硬度（R 级） | Average value: 115 Grade Count:9 | ||
| 肖氏硬度 (邵氏 D) | Average value: 80.5 Grade Count:4 | ||
| 球压硬度 | MPa | psi | Average value: 151 MPa Grade Count:10 |
| 极限抗拉强度 | MPa | psi | Average value: 68.4 MPa Grade Count:58 |
| MPa @Temperature -40.0 - 150 °C | psi @Temperature -40.0 - 302 °F | Average value: 40.3 MPa Grade Count:6 | |
| 抗张强度(屈服) | MPa | psi | Average value: 72.4 MPa Grade Count:24 |
| 伸长率 (断裂) | Average value: 14.1 % Grade Count:66 | ||
| @Temperature 60.0 - 150 °C | @Temperature 140 - 302 °F | Average value: 16.2 % Grade Count:2 | |
| 屈服伸长率 | Average value: 9.84 % Grade Count:9 | ||
| 弹性模量 | GPa | ksi | Average value: 4.66 GPa Grade Count:52 |
| GPa @Temperature -20.0 - 150 °C | ksi @Temperature -4.00 - 302 °F | Average value: 2.18 GPa Grade Count:3 | |
| 弯曲强度 | MPa | psi | Average value: 114 MPa Grade Count:44 |
| MPa @Temperature -40.0 - 80.0 °C | psi @Temperature -40.0 - 176 °F | Average value: 114 MPa Grade Count:1 | |
| 弯曲模量 | GPa | ksi | Average value: 4.41 GPa Grade Count:50 |
| GPa @Temperature -40.0 - 120 °C | ksi @Temperature -40.0 - 248 °F | Average value: 2.65 GPa Grade Count:4 | |
| 悬壁梁缺口冲击强度 | J/cm | ft-lb/in | Average value: 0.673 J/cm Grade Count:24 |
| J/cm @Temperature -40.0 - -20.0 °C | ft-lb/in @Temperature -40.0 - -4.00 °F | Average value: 0.416 J/cm Grade Count:3 | |
| kJ/m² | ft-lb/in² | Average value: 7.65 kJ/m² Grade Count:18 | |
| kJ/m² @Temperature -30.0 - -30.0 °C | ft-lb/in² @Temperature -22.0 - -22.0 °F | Average value: 5.67 kJ/m² Grade Count:3 | |
| 悬壁梁无缺口冲击强度 | kJ/m² @Temperature -30.0 - -30.0 °C | ft-lb/in² @Temperature -22.0 - -22.0 °F | Average value: 35.0 kJ/m² Grade Count:1 |
| 简支梁无缺口冲击强度 | J/cm² - NB | ft-lb/in² - NB | Average value: 7.57 J/cm² Grade Count:51 |
| J/cm² - NB @Temperature -40.0 - 30.0 °C | ft-lb/in² - NB @Temperature -40.0 - 86.0 °F | Average value: 5.41 J/cm² Grade Count:27 | |
| 简支梁缺口冲击强度 | J/cm² | ft-lb/in² | Average value: 0.701 J/cm² Grade Count:44 |
| J/cm² @Temperature -30.0 - 30.0 °C | ft-lb/in² @Temperature -22.0 - 86.0 °F | Average value: 0.430 J/cm² Grade Count:22 | |
| 拉伸蠕变模量(1000 hr) | MPa | psi | Average value: 785 MPa Grade Count:4 |
| 电气性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 电阻率 | ohm-cm | ohm-cm | Average value: 7.42e+14 ohm-cm Grade Count:41 |
| 表面电阻 | ohm | ohm | Average value: 1.45e+15 ohm Grade Count:23 |
| 介电常数 | Average value: 5.03 Grade Count:18 | ||
| 介电强度 | kV/mm | kV/in | Average value: 29.3 kV/mm Grade Count:24 |
| 耗散因数 | Average value: 0.0868 Grade Count:17 | ||
| 耐电弧性 | sec | sec | Average value: 155 sec Grade Count:3 |
| 相比耐漏电起痕指数(CTI) | V | V | Average value: 475 V Grade Count:43 |
| 热性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 线性热膨胀系数 | µm/m-°C | µin/in-°F | Average value: 58.5 µm/m-°C Grade Count:30 |
| 线性热膨胀系数,横向流动 | µm/m-°C | µin/in-°F | Average value: 61.4 µm/m-°C Grade Count:16 |
| 导热系数 | W/m-K | BTU-in/hr-ft²-°F | Average value: 0.310 W/m-K Grade Count:6 |
| 熔融温度 | °C | °F | Average value: 220 °C Grade Count:61 |
| 最高工作温度, Air | °C | °F | Average value: 129 °C Grade Count:18 |
| 载荷下热变形温度(0.46 MPa) | °C | °F | Average value: 201 °C Grade Count:37 |
| 载荷下热变形温度(1.8 MPa) | °C | °F | Average value: 122 °C Grade Count:64 |
| 载荷下热变形温度(8.0 MPa) | °C | °F | Average value: 50.0 °C Grade Count:3 |
| 维卡软化温度 | °C | °F | Average value: 207 °C Grade Count:22 |
| 分解温度 | °C | °F | Average value: 300 °C Grade Count:4 |
| UL RTI | °C | °F | Average value: 108 °C Grade Count:11 |
| UL RTI，机械冲击 | °C | °F | Average value: 90.7 °C Grade Count:11 |
| UL RTI，机械无冲击 | °C | °F | Average value: 108 °C Grade Count:11 |
| 可燃性(UL94) | Grade Count:59 |