| 物理性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 比重 | g/cc | g/cc | ASTM D792 |
| 密度 | g/cc | lb/in³ | ASTM D792 |
| g/cc | lb/in³ | ISO 1183 | |
| 吸水率 | @Time 86400 sec | @Time 24.0 hour | ASTM D570 |
| 水分吸收 | 23°C / 50% RH; ISO 62 | ||
| 饱和吸水率 | ISO 62 | ||
| 线性成型收缩率,Flow | cm/cm @Thickness 3.20 mm | in/in @Thickness 0.126 in | SABIC Method |
| 熔体流动速率 | g/10 min @Load 1.20 kg, Temperature 300 °C | g/10 min @Load 2.65 lb, Temperature 572 °F | ASTM D1238 |
| 化合物熔体指数 | g/10 min @Load 1.20 kg, Temperature 300 °C | g/10 min @Load 2.65 lb, Temperature 572 °F | MVR [cm^3/10 min]; ISO 1133 |
| 机械性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 洛氏硬度（M 级） | ASTM D785 | ||
| 洛氏硬度（R 级） | ASTM D785 | ||
| 抗张强度(断裂) | MPa | psi | 50 mm/min; ISO 527 |
| MPa | psi | Type I, 50 mm/min; ASTM D638 | |
| 抗张强度(屈服) | MPa | psi | Type I, 50 mm/min; ASTM D638 |
| MPa | psi | 50 mm/min; ISO 527 | |
| 伸长率 (断裂) | Type I, 50 mm/min; ASTM D638 | ||
| 50 mm/min; ISO 527 | |||
| 屈服伸长率 | 50 mm/min; ISO 527 | ||
| Type I, 50 mm/min; ASTM D638 | |||
| 拉伸模量 | GPa | ksi | 5 mm/min; ASTM D638 |
| GPa | ksi | 1 mm/min; ISO 527 | |
| 弯曲强度 | MPa | psi | 2 mm/min; ISO 178 |
| MPa | psi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| 弯曲模量 | GPa | ksi | 2 mm/min; ISO 178 |
| GPa | ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| 悬壁梁缺口冲击强度 | J/cm | ft-lb/in | ASTM D256 |
| J/cm @Temperature -30.0 °C | ft-lb/in @Temperature -22.0 °F | ASTM D256 | |
| 悬壁梁无缺口冲击强度 | J/cm | ft-lb/in | ASTM D4812 |
| 拉伸冲击强度 | kJ/m² | ft-lb/in² | Type S; ASTM D1822 |
| 落锤总能量 | J | ft-lb | ASTM D3029 |
| J @Temperature 23.0 °C | ft-lb @Temperature 73.4 °F | ASTM D3763 |
| 电气性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 体积电阻率 | >= ohm-cm | >= ohm-cm | ASTM D257 |
| 介电常数 | @Frequency 1.00e+6 Hz | @Frequency 1.00e+6 Hz | ASTM D150 |
| @Frequency 50.0 - 60.0 Hz | @Frequency 50.0 - 60.0 Hz | ASTM D150 | |
| 介电强度 | kV/mm @Thickness 3.20 mm | kV/in @Thickness 0.126 in | in air; ASTM D149 |
| 耗散因数 | @Frequency 50.0 - 60.0 Hz | @Frequency 50.0 - 60.0 Hz | ASTM D150 |
| @Frequency 100 Hz | @Frequency 100 Hz | ASTM D150 | |
| 耐电弧性 | sec | sec | Tungsten; ASTM D495 |
| 相比耐漏电起痕指数(CTI) | V | V | UL 746A |
| 热丝引燃 (HWI) | sec | sec | UL 746A |
| 高电弧燃烧，HAI | arcs | arcs | UL 746A |
| 高压电弧跟踪率，HVTR | mm/min | in/min | UL 746A |
| 热性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 线形热膨胀系数 - 流动 | µm/m-°C @Temperature -40.0 - 40.0 °C | µin/in-°F @Temperature -40.0 - 104 °F | ASTM E 831 |
| µm/m-°C @Temperature -40.0 - 40.0 °C | µin/in-°F @Temperature -40.0 - 104 °F | ISO 11359-2 | |
| 线性热膨胀系数,横向流动 | µm/m-°C @Temperature -40.0 - 40.0 °C | µin/in-°F @Temperature -40.0 - 104 °F | ASTM E 831 |
| µm/m-°C @Temperature -40.0 - 40.0 °C | µin/in-°F @Temperature -40.0 - 104 °F | ISO 11359-2 | |
| 比热容 | J/g-°C | BTU/lb-°F | ASTM C351 |
| 导热系数 | W/m-K | BTU-in/hr-ft²-°F | ASTM C177 |
| 载荷下热变形温度(1.8 MPa) | °C | °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| °C @Thickness 3.20 mm | °F @Thickness 0.126 in | unannealed; ASTM D648 | |
| 维卡软化温度 | °C | °F | Rate B/50; ISO 306 |
| °C | °F | Rate B/120; ISO 306 | |
| °C | °F | Rate B/50; ASTM D1525 | |
| UL RTI | °C | °F | UL 746B |
| UL RTI，机械冲击 | °C | °F | UL 746B |
| UL RTI，机械无冲击 | °C | °F | UL 746B |
| 可燃性(UL94) | @Thickness 1.47 mm | @Thickness 0.0579 in | UL 94 |
| 光学性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 折射率 | ASTM D542 | ||
| 雾度 | @Thickness 2.54 mm | @Thickness 0.100 in | ASTM D1003 |
| Transmission, Visible | 2.54 mm; ASTM D1003 |
| 材料描述 | 测试方法 | |
|---|---|---|
| Specific Volume | 0.83cm^3/g | ASTM D792 |