Information provided by Diamond Polymers, Inc.
| 物理性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 比重 | g/cc | g/cc | ASTM D792 |
| 线性成型收缩率 | cm/cm | in/in | ASTM D955 |
| 熔体流动速率 | g/10 min @Load 5.00 kg, Temperature 200 °C | g/10 min @Load 11.0 lb, Temperature 392 °F | Procedure A Condition G; ASTM D1238 |
| g/10 min @Load 3.80 kg, Temperature 230 °C | g/10 min @Load 8.38 lb, Temperature 446 °F | Procedure A Condition I; ASTM D1238 |
| 机械性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 洛氏硬度（R 级） | ASTM D785 | ||
| 抗张强度(屈服) | MPa | psi | chs 2 in/min; ASTM D638 |
| 弯曲模量 | GPa | ksi | Tangent, chs 0.05 in/min; ASTM D790 |
| 悬壁梁缺口冲击强度 | J/cm @Thickness 3.17 mm, Temperature 23.0 °C | ft-lb/in @Thickness 0.125 in, Temperature 73.4 °F | bar; ASTM D256 |
| 热性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 载荷下热变形温度(1.8 MPa) | °C | °F | 0.125 in bar Unannealed/Conditioned 48 hours at 23°C; ASTM D648 |
| °C | °F | 0.125 in bar Annealed 4 hours at 80°C; ASTM D648 | |
| 维卡软化温度 | °C | °F | 0.125 inch, 1 Kg; ASTM D1525 |
| 可燃性(UL94) | @Thickness 1.50 mm | @Thickness 0.0591 in |
| 加工性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 料筒中部温度 | °C | °F | |
| 模具温度 | °C | °F | Higher mold temperature provides a product with excellent surface finishing and less residual stress. |
| 干燥温度 | °C | °F | |
| 干燥时间 | hour | hour | |
| 注射压力 | MPa | psi |