物理性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
---|---|---|---|
比重 | g/cc | g/cc | ASTM D792 |
机械性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
---|---|---|---|
肖氏硬度 (邵氏 D) | 15 sec; ASTM D2240 | ||
抗张强度(屈服) | MPa | psi | Type I, 5.1 mm/min; ASTM D638 |
拉伸模量 | GPa | ksi | Type I, 5.1 mm/min; ASTM D638 |
弯曲强度 | MPa | psi | ASTM D790 |
弯曲模量 | GPa | ksi | ASTM D790 |
悬壁梁缺口冲击强度 | J/cm @Thickness 3.18 mm, Temperature 23.0 °C | ft-lb/in @Thickness 0.125 in, Temperature 73.4 °F | Compression Molded, Across Flow; ASTM D256A |
J/cm @Thickness 3.18 mm, Temperature 23.0 °C | ft-lb/in @Thickness 0.125 in, Temperature 73.4 °F | Compression Molded, Flow; ASTM D256A | |
J/cm @Thickness 3.18 mm, Temperature 23.0 °C | ft-lb/in @Thickness 0.125 in, Temperature 73.4 °F | Injection Molded; ASTM D256A | |
Dart Drop Total Energy | J/cm @Temperature 23.0 °C | ft-lb/mil @Temperature 73.4 °F | Procedure A, C.125; ASTM D4226 |
J/cm @Temperature 23.0 °C | ft-lb/mil @Temperature 73.4 °F | Procedure B, C.125; ASTM D4226 |
热性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
---|---|---|---|
线形热膨胀系数 - 流动 | µm/m-°C | µin/in-°F | ASTM D696 |
载荷下热变形温度(1.8 MPa) | °C @Thickness 3.18 mm | °F @Thickness 0.125 in | Unannealed; ASTM D648 |
加工性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
---|---|---|---|
加工(熔体)温度 | °C | °F |
材料描述 | 测试方法 | |
---|---|---|
Ease of Sizing | Good | |
特性 | General Purpose | |
High Impact Resistance | ||
形式 | Pellets | |
通用材料 | PVC, Rigid | |
通用名 | Polyvinyl Chloride, Rigid (PVC, Rigid) | |
加工方法 | Extrusion | |
PVC Cell Classification | 16364 | ASTM D1784 |
供货地区 | Africa & Middle East | |
Asia Pacific | ||
Europe | ||
North America | ||
South America | ||
用途 | General Purpose | |
Profiles |