China PPS hFR42

PPS-hFR42 is filled PPS compound, which is filled with mineral based on the PPS resin. It shows high rigidity, creep resistance, high-temperature resistance, inherent flame resistance, chemical resistance, excellent electrical insulation properties, arc resistance, low water absorption, easy processing, low mold shrinkage, good dimensional stability, and radiation resistance. Its colour is offwhite.

Owing to its high performance and light colour, it's an excellent selection for outer decorating parts with high temperature resistance and high rigidity in electronic/electric and medical industry. Such as: outer shells of apparatus and electric appliance, connectors, high-temperature disinfectant instruments, surgical containers, shells of the electric tooth-cleaning devices and other devices used in dentistry.

基本信息
填料/增强材料	矿物填料
特性	尺寸稳定性良好 刚性，高 绝缘 抗电弧 抗伽马辐射 可加工性，良好 良好的抗蠕变性 耐化学性良好 耐热性，高 收缩性低 吸水低或不吸水 阻燃性
用途	电气/电子应用领域 家电部件 容器 牙齿应用领域 医疗/护理用品 装饰部件
外观	类白色
加工方法	注射成型

物理性能	额定值	单位制	测试方法
密度		g/cm³	内部方法
收缩率 - 流动		%	内部方法

机械性能	额定值	单位制	测试方法
抗张强度		MPa	内部方法
伸长率 (断裂)		%	内部方法
弯曲模量		MPa	内部方法
弯曲强度		MPa	内部方法

冲击性能	额定值	单位制	测试方法
悬壁梁缺口冲击强度		kJ/m²	内部方法

热性能	额定值	单位制	测试方法
载荷下热变形温度 (1.8 MPa, 未退火)		°C	内部方法
熔融温度		°C	内部方法

电气性能	额定值	单位制	测试方法
表面电阻率		ohms	内部方法
体积电阻率		ohms·cm	内部方法

可燃性	额定值	单位制	测试方法
UL 阻燃等级			内部方法

注射	额定值	单位制
干燥温度		°C
干燥时间		hr
料筒后部温度		°C
料筒中部温度		°C
料筒前部温度		°C
射嘴温度		°C
加工（熔体）温度		°C
模具温度		°C
注塑压力		MPa
背压		MPa
螺杆转速		rpm

注射说明
Processing time: 4 to 8hr