LG Chemical LUPOL HF5157Z PP+Rubber+MF, High Flow and Stiffness, High Impact

Polymer,Thermoplastic,Polypropylene (PP),Polypropylene, Mineral Reinforced, Impact Modified

LG Chemical

PDF物性文档下载

产品说明:

Description: Injection Molding, PP+Rubber+MF, High Flow and Stiffness, High Impact, Good Paintability

Application: Automotive Exterior (Slim wall Bumper Fascia)

Information provided by LG Chemical

LG Chemical LUPOL HF5157Z PP+Rubber+MF, High Flow and Stiffness, High Impact 物性表
物理性能额定值 (公制)额定值 (英制)测试方法
比重 g/cc g/cc ASTM D792
处理 Injection Molding
线性成型收缩率,Flow cm/cm
@Thickness 3.20 mm
in/in
@Thickness 0.126 in
ASTM D955
熔体流动速率 g/10 min
@Load 2.16 kg, Temperature 230 °C
g/10 min
@Load 4.76 lb, Temperature 446 °F
ASTM D1238
机械性能额定值 (公制)额定值 (英制)测试方法
抗张强度(屈服) MPa
@Thickness 3.20 mm
psi
@Thickness 0.126 in
50mm/min; ASTM D638
伸长率 (断裂)
@Thickness 3.20 mm
@Thickness 0.126 in
50mm/min; ASTM D638
弯曲强度 MPa
@Thickness 6.40 mm
psi
@Thickness 0.252 in
10mm/min; ASTM D790
弯曲模量 GPa
@Thickness 6.40 mm
ksi
@Thickness 0.252 in
10mm/min; ASTM D790
悬壁梁缺口冲击强度>= J/cm
@Thickness 6.40 mm, Temperature -10.0 °C
>= ft-lb/in
@Thickness 0.252 in, Temperature 14.0 °F
ASTM D256
>= J/cm
@Thickness 6.40 mm, Temperature 23.0 °C
>= ft-lb/in
@Thickness 0.252 in, Temperature 73.4 °F
ASTM D256
热性能额定值 (公制)额定值 (英制)测试方法
载荷下热变形温度(0.46 MPa) °C
@Thickness 6.40 mm
°F
@Thickness 0.252 in
Unannealed; ASTM D648
加工性能额定值 (公制)额定值 (英制)测试方法
料筒后部温度 °C °F Injection Molding
料筒中部温度 °C °F Injection Molding
料筒前部温度 °C °F Injection Molding
射嘴温度 °C °F Injection Molding
加工(熔体)温度 °C °F Injection Molding
模具温度 °C °F Injection Molding
干燥温度 °C °F Injection Molding
干燥时间 hour hour Injection Molding
背压 MPa psi Injection Molding
螺杆转速 rpm rpm Injection Molding