Information provided by Dow
This product line was spun off from Dow Chemical to Styron in 2010.| 物理性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 比重 | g/cc | g/cc | ASTM D792 |
| 吸水率 | 23°C, 24hrs; ASTM D570 | ||
| 饱和吸水率 | 23°C, 50% RH; ASTM D570 | ||
| 线性成型收缩率 | cm/cm | in/in | ASTM D955 |
| 熔体流动速率 | g/10 min @Load 1.20 kg, Temperature 300 °C | g/10 min @Load 2.65 lb, Temperature 572 °F | ASTM D1238 |
| 机械性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 洛氏硬度（M 级） | ASTM D785 | ||
| 洛氏硬度（R 级） | ASTM D785 | ||
| 极限抗拉强度 | MPa | psi | ASTM D638 |
| 抗张强度(屈服) | MPa | psi | ASTM D638 |
| 伸长率 (断裂) | ASTM D638 | ||
| 拉伸模量 | GPa | ksi | 2 in/min; ASTM D638 |
| 弯曲强度 | MPa | psi | ASTM D790 |
| 弯曲模量 | GPa | ksi | ASTM D790 |
| 悬壁梁缺口冲击强度 | J/cm | ft-lb/in | 0.125 in; 10 mil notch; ASTM D256 |
| 悬壁梁无缺口冲击强度 | ASTM D256 | ||
| 拉伸冲击强度 | kJ/m² | ft-lb/in² | ASTM D1822, Type S |
| 落锤总能量 | J @Thickness 3.20 mm | ft-lb @Thickness 0.126 in | 203 m/min; ASTM D1822 |
| 电气性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 体积电阻率 | ohm-cm | ohm-cm | ASTM D257 |
| 介电常数 | @Frequency 60 Hz | @Frequency 60 Hz | ASTM D150 |
| @Frequency 1e+6 Hz | @Frequency 1e+6 Hz | ASTM D150 | |
| 介电强度 | kV/mm | kV/in | ASTM D149 |
| 耗散因数 | @Frequency 60 Hz | @Frequency 60 Hz | ASTM D150 |
| @Frequency 1e+6 Hz | @Frequency 1e+6 Hz | ASTM D150 |
| 热性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 线性热膨胀系数 | µm/m-°C @Temperature -40.0 - 82.2 °C | µin/in-°F @Temperature -40.0 - 180 °F | ASTM D696 |
| 载荷下热变形温度(0.46 MPa) | °C | °F | annealed; ASTM D648 |
| 载荷下热变形温度(1.8 MPa) | °C | °F | Unannealed, 0.125 in; ASTM D648 |
| °C | °F | annealed; ASTM D648 | |
| 维卡软化温度 | °C | °F | 50°C/hr, 50N Load; ASTM D1525 |
| 可燃性(UL94) | 0.0625 in | ||
| 0.125 in | |||
| Flammability Test | [inches] Average Extent of Burning; ASTM D635 | ||
| 极限氧指数 | ASTM D2863 |
| 光学性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 折射率 | ASTM D542 | ||
| 雾度 | ASTM D1003 | ||
| Transmission, Visible | ASTM D1003 |