SABIC Innovative Plastics LNP THERMOCOMP EXTC8143 PC (Asia Pacific)

Polycarbonate (PC)

SABIC Innovative Plastics (GE Plastics)

产品说明

LNP* Thermocomp* EXTC8143 is a compound based on Polycarbonate resin containing Glass Fiber, Flame Retardant. Added features of this material include: High modulus, good flatness, good ductility, Non-Brominated & Non-Chlorinated Flame Retardant.

物理性能额定值 (公制)额定值 (英制)测试方法
密度 g/cc lb/in³ ASTM D792
线性成型收缩率,Flow cm/cm
@Time 86400 sec
in/in
@Time 24.0 hour
ASTM D955
线性成型收缩率,横向 cm/cm
@Time 86400 sec
in/in
@Time 24.0 hour
ASTM D955
化合物熔体指数 g/10 min
@Load 2.16 kg, Temperature 300 °C
g/10 min
@Load 4.76 lb, Temperature 572 °F
MVR [cm^3/10 min]; ISO 1133
机械性能额定值 (公制)额定值 (英制)测试方法
抗张强度(断裂) MPa psi Type I, 5 mm/min; ASTM D638
伸长率 (断裂) Type I, 5 mm/min; ASTM D638
拉伸模量 GPa ksi 5 mm/min; ASTM D638
弯曲强度 MPa psi 1.3 mm/min, 50 mm span; ASTM D790
弯曲模量 GPa ksi 1.3 mm/min, 50 mm span; ASTM D790
悬壁梁缺口冲击强度 J/cm ft-lb/in ASTM D256
悬壁梁无缺口冲击强度 J/cm ft-lb/in ASTM D4812
简支梁无缺口冲击强度 J/cm² ft-lb/in² Edgew 80*10*4 sp=62mm; ISO 179/1eU
简支梁缺口冲击强度 J/cm² ft-lb/in² Edgew 80*10*4 sp=62mm; ISO 179/1eA
落锤总能量 J ft-lb Instrumented Impact Energy @ peak; ASTM D3763
热性能额定值 (公制)额定值 (英制)测试方法
载荷下热变形温度(1.8 MPa) °C
@Thickness 3.20 mm
°F
@Thickness 0.126 in
unannealed; ASTM D648
可燃性(UL94)
@Thickness 0.800 mm
@Thickness 0.0315 in
UL 94
Copyright © souwuxing.com All Rights Reserved. 归 搜聚信息科技公司 所有
此数据表中的信息由 搜聚 从该材料的生产商处获得。搜聚 尽最大努力确保此数据的准确性。 但是 搜聚 对这些数据值不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。