Mylar® type WC11 films combine the tensile strength, dimensional stability, and dielectric strength needed for wire and cable applications.
Typical Applications: Mylar® Type WC11 films possess the characteristics required for wire and cable used in telecommunications and power transmission fields.
Approvals: UL 94 VTM-2 - for 142 - 300 gauge (0.036 - 0.076 mm)
Information provided by DuPont.物理性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
---|---|---|---|
密度 | g/cc | lb/in³ | Typical Mylar®; ASTM D1505 |
机械性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
---|---|---|---|
断裂伸长率,MD | ASTM D882A | ||
断裂伸长率,TD | ASTM D882A | ||
抗张强度(MD : 断裂) | MPa | psi | ASTM D882A |
抗张强度(TD : 断裂) | MPa | psi | ASTM D882A |
电气性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
---|---|---|---|
介电强度 | kV/mm | kV/in | 1/4" electrode 500 V/sec 25°C in air; ASTM D149 |
介电击穿 | V | V | 1/4" electrode 500 V/sec 25°C in air; ASTM D149 |
热性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
---|---|---|---|
比热容 | J/g-°C | BTU/lb-°F | Typical Mylar® |
熔融温度 | °C | °F | Typical Mylar® via DSC |
收缩,MD | @Temperature 150 °C, Time 1800 sec | @Temperature 302 °F, Time 0.500 hour | Unrestrained |
收缩,TD | @Temperature 150 °C, Time 1800 sec | @Temperature 302 °F, Time 0.500 hour | Unrestrained |
光学性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
---|---|---|---|
雾度 | ASTM D1003 |
材料描述 | 测试方法 | |
---|---|---|
Yield (nominal) | 6900 in2/lb |