Benefits: This product offers all the primary properties of unreinforced polyamide 66. In addition it has improved resistance to high temperature and it can be used for components which have to withstand mid term temperature stresses. This product can also be vacuum metalized with very good surface quality and adhesion of the aluminum surface. In case of fire its smoke rate is very low. It is also complying with NFF 16-101 rating I3 F2.
Available in: Asia Pacific and Europe
Regulations compliance: Grades produced or imported in Europe comply with directive 453/2010/EC, which amends REACH directive 1907/2006/EC. This grade complies with RoHS directive 2002/95/EC. Unless specified, this grade is not suitable for food contact, medical devices or toy applications
Applications: It perfectly suits for the production of the head lamp bezels in automotive industry and connectors in electrical industry.
Information provided by Rhodia, Rhodia has been acquired by Solvay.| 物理性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 密度 | g/cc | lb/in³ | ISO 1183/A |
| Water Absorption | @Temperature 23.0 °C, Time 86400 sec | @Temperature 73.4 °F, Time 24.0 hour | ISO 62 |
| @Temperature 100 °C, Time 1800 sec | @Temperature 212 °F, Time 0.500 hour | ISO 62 | |
| 线性成型收缩率 | cm/cm | in/in | Isotropy |
| 线性成型收缩率,Flow | cm/cm | in/in | |
| 线性成型收缩率，横向 | cm/cm | in/in |
| 机械性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 抗张强度(断裂) | MPa | psi | ISO 527 Type 1A |
| 抗张强度 | MPa @Strain 2.00 % | psi @Strain 2.00 % | |
| MPa @Strain 4.00 % | psi @Strain 4.00 % | ||
| MPa @Strain 6.00 % | psi @Strain 6.00 % | ||
| 抗张强度(屈服) | MPa | psi | ASTM D638 |
| MPa | psi | ISO 527 type 1 A | |
| 伸长率 (断裂) | ISO 527 Type 1A | ||
| ASTM D638 | |||
| 拉伸模量 | GPa | ksi | ISO 527 Type 1A |
| 弯曲强度 | MPa | psi | ASTM D790 |
| MPa | psi | ISO 178 | |
| 弯曲模量 | GPa | ksi | ISO 178 |
| GPa | ksi | ASTM D790 | |
| 悬壁梁缺口冲击强度 | kJ/m² | ft-lb/in² | ISO 180/1A |
| kJ/m² | ft-lb/in² | ASTM D256 | |
| 悬壁梁无缺口冲击强度 | ISO 180/1U | ||
| 简支梁无缺口冲击强度 | ISO 179/1eU | ||
| 简支梁缺口冲击强度 | J/cm² | ft-lb/in² | ISO 179/1eA |
| 热性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 熔融温度 | °C | °F | ISO 11357 |
| 载荷下热变形温度(0.46 MPa) | °C | °F | ASTM D648 |
| 载荷下热变形温度(1.8 MPa) | °C | °F | ISO 75/Af |
| 可燃性(UL94) | @Thickness 1.60 mm | @Thickness 0.0630 in | 1210 |
| @Thickness 3.20 mm | @Thickness 0.126 in | 1210 | |
| 极限氧指数 | ISO 4589 | ||
| 灼热丝易燃指数 | °C @Thickness 0.800 mm | °F @Thickness 0.0315 in | ISO 60695-2-12 |
| °C @Thickness 1.60 mm | °F @Thickness 0.0630 in | ISO 60695-2-12 | |
| °C @Thickness 1.60 mm | °F @Thickness 0.0630 in | Ignition Temperature; ISO 60695-2-13 |
| 加工性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 进料温度 | °C | °F | |
| 模具温度 | °C | °F | |
| 干燥温度 | °C | °F | |
| 水分含量 |
| 材料描述 | 测试方法 | |
|---|---|---|
| Compression Zone | 270-280°C | |
| Mixing Zone | 280-290°C |