DSM Arnite® T08 200 (extrusion) PBT (European and Asian Grade)

Arnite resins are engineered to provide specific performance in applications where DSM technology can offer value.

Arnite Molding resins:

• Standard Unfilled and Reinforced materials
• High modulus Flame retardant grades
• Easy molding FR grades for connectors
• Toughened unfilled materials for durability
• High modulus, tight specification for critical auto components
• Toughened reinforced resins
• Low outgassing grades for reflector surfaces

Arnite extrusion resins: Specialized materials for specific uses

• PET for medical applications
• Loose buffer Optical fiber tubing
• PET for stock shapes

Applications

• Automotive:Connectors, sensors and E&E parts, Exterior fittings, Gear housings and motors, Brake valve bodies
• Electrical & Electronic: Telecoms and IT connectors, Bobbins, Low voltage Power distribution, E-motor components, Lightings and Lamp fittings
• Consumer Durables: Small Appliances
• Other: Optical fiber tubing

Information provided by DSM.

物理性能	额定值 (公制)	额定值 (英制)	测试方法
密度	g/cc	lb/in³	ISO 1183
吸水率			Sim. to ISO 62
平衡吸湿			Humidity Absorption; Sim. to ISO 62
熔体流动速率	g/10 min @Load 2.16 kg, Temperature 250 °C	g/10 min @Load 4.76 lb, Temperature 482 °F	Calculated from Volume Flow Rate of 10 cm<sup>3</sup>/10min.; ISO 1133

机械性能	额定值 (公制)	额定值 (英制)	测试方法
抗张强度(屈服)	MPa	psi	ISO 527-1/-2
伸长率 (断裂)			ISO 527-1/-2
屈服伸长率			ISO 527-1/-2
拉伸模量	GPa	ksi	ISO 527-1/-2
简支梁无缺口冲击强度	@Temperature -30.0 °C	@Temperature -22.0 °F	ISO 179/1eU
	@Temperature 23.0 °C	@Temperature 73.4 °F	ISO 179/1eU
简支梁缺口冲击强度	J/cm² @Temperature -30.0 °C	ft-lb/in² @Temperature -22.0 °F	ISO 179/1eA
	J/cm² @Temperature 23.0 °C	ft-lb/in² @Temperature 73.4 °F	ISO 179/1eA

电气性能	额定值 (公制)	额定值 (英制)	测试方法
体积电阻率	>= ohm-cm	>= ohm-cm	IEC 60093
表面电阻	>= ohm	>= ohm	IEC 60093
介电常数	@Frequency 1e+6 Hz	@Frequency 1e+6 Hz	IEC 60250
	@Frequency 100 Hz	@Frequency 100 Hz	IEC 60250
介电强度	kV/mm	kV/in	IEC 60243-1
耗散因数	@Frequency 100 Hz	@Frequency 100 Hz	IEC 60250
	@Frequency 1e+6 Hz	@Frequency 1e+6 Hz	IEC 60250
相比耐漏电起痕指数(CTI)	V	V	IEC 60112
	>= V	>= V	PLC 0; UL 746A

热性能	额定值 (公制)	额定值 (英制)	测试方法
线形热膨胀系数 - 流动	µm/m-°C @Temperature 20.0 °C	µin/in-°F @Temperature 68.0 °F	ISO 11359-1/-2
线性热膨胀系数,横向流动	µm/m-°C @Temperature 20.0 °C	µin/in-°F @Temperature 68.0 °F	ISO 11359-1/-2
熔融温度	°C	°F	10°C/min; ISO 11357-1/-3
载荷下热变形温度(0.46 MPa)	°C	°F	ISO 75-1/-2
载荷下热变形温度(1.8 MPa)	°C	°F	ISO 75-1/-2
UL RTI	°C @Thickness 1.50 mm	°F @Thickness 0.0591 in	UL746B
	°C @Thickness 0.750 mm	°F @Thickness 0.0295 in	UL746B
UL RTI，机械冲击	°C @Thickness 0.750 mm	°F @Thickness 0.0295 in	UL746B
	°C @Thickness 1.50 mm	°F @Thickness 0.0591 in	UL746B
UL RTI，机械无冲击	°C @Thickness 0.750 mm	°F @Thickness 0.0295 in	UL746B
	°C @Thickness 1.50 mm	°F @Thickness 0.0591 in	UL746B
可燃性(UL94)	@Thickness 1.60 mm	@Thickness 0.0630 in	IEC 60695-11-10
	@Thickness 0.750 mm	@Thickness 0.0295 in	IEC 60695-11-10

材料描述		测试方法
注塑	Yes
Other Extrusion	Yes
Without Fillers	Yes