Nilit Nilamid A3 H G3 ZB 13% Glass Reinforced High Impact PA66

Polymer,Thermoplastic,Nylon,Nylon 66,Nylon 66, 10% Glass Fiber Filled

Nilit

PDF物性文档下载

产品说明:

Description: Nilamid A3 H G3 ZB (13% Glass Reinforced) was developed for applications that require a combination of high stiffness and good elongation or impact resistance. It is widely used for applications that need the strength and stiffness of reinforced polyamide, but also need to be snap fitted.

Key characteristics:

Information provided by NILIT.

Nilit Nilamid A3 H G3 ZB 13% Glass Reinforced High Impact PA66 物性表
物理性能额定值 (公制)额定值 (英制)测试方法
密度 g/cc lb/in³ ASTM D792, ISO 1183
吸水率 23°C, 24h in H<sub>2</sub>O; sim. ISO 62
饱和吸水率 sim. ISO 62
线性成型收缩率,Flow cm/cm in/in Euronil
线性成型收缩率,横向 cm/cm in/in Euronil
机械性能额定值 (公制)额定值 (英制)测试方法
抗张强度(屈服) MPa psi ISO 527, ASTM D638
伸长率 (断裂) ISO 527, ASTM D638
弯曲强度 MPa psi ISO 178, ASTM D790
弯曲模量 GPa ksi ISO 178, ASTM D790
悬壁梁缺口冲击强度 kJ/m²
@Temperature -30.0 °C
ft-lb/in²
@Temperature -22.0 °F
ISO 180/1A
kJ/m²
@Temperature 23.0 °C
ft-lb/in²
@Temperature 73.4 °F
ISO 180/1A
简支梁缺口冲击强度 J/cm² ft-lb/in² ISO 179
电气性能额定值 (公制)额定值 (英制)测试方法
Comparative Tracking Index V
@Thickness 3.20 mm
V
@Thickness 0.126 in
Sol. B; IEC 112, UL 746A
V
@Thickness 3.20 mm
V
@Thickness 0.126 in
Sol. A; IEC 112, UL 746A
热性能额定值 (公制)额定值 (英制)测试方法
最高工作温度, Air °C °F 20,000 hr; IEC 216
载荷下热变形温度(1.8 MPa) °C °F ISO 75, ASTM D648
维卡软化温度 °C °F 49 N; ISO 306, ASTM D1525
°C °F 9.8 N; ISO 306, ASTM D1525
可燃性(UL94)
@Thickness 0.800 mm
@Thickness 0.0315 in
@Thickness 3.20 mm
@Thickness 0.126 in
灼热丝易燃指数 °C
@Thickness 3.20 mm
°F
@Thickness 0.126 in
Glow Wire Flammability Index; IEC 694-2-12
°C
@Thickness 0.800 mm
°F
@Thickness 0.0315 in
Glow Wire Flammability Index; IEC 694-2-12
加工性能额定值 (公制)额定值 (英制)测试方法
射嘴温度 °C °F
1区 °C °F hopper
2区 °C °F
3区 °C °F
4区 °C °F
加工(熔体)温度 °C °F Do not melt above 300°C
模具温度 °C °F Preferred
干燥温度 °C °F
干燥时间 hour hour
注射压力 MPa psi
材料描述测试方法
Clamping Forcein tons, 0.7 times the projected surface area in cm2
Heat Resistance - Ball TestOKat 125°C, IEC 309
OKat 165°C, IEC 309
Holding Pressure90 Mpa