SABIC Innovative Plastics LNP LUBRILOY D2000P PC (Asia Pacific)

Polymer,Thermoplastic,Polycarbonate (PC)

SABIC Innovative Plastics (GE Plastics)

PDF物性文档下载

产品说明:

LNP LUBRILOY* D2000P is a compound based on Polycarbonate resin containing Proprietary Lubricant. Added features of this material include: Exceptional Processing.

SABIC Innovative Plastics LNP LUBRILOY D2000P PC (Asia Pacific) 物性表
物理性能额定值 (公制)额定值 (英制)测试方法
密度 g/cc lb/in³ ASTM D792
g/cc lb/in³ ISO 1183
水分吸收 50% RH, 24 hrs; ASTM D570
23°C / 50% RH; ISO 62
线性模具收缩,Flow cm/cm
@Time 86400 sec
in/in
@Time 24.0 hour
ASTM D955
cm/cm
@Time 86400 sec
in/in
@Time 24.0 hour
ISO 294
线性成型收缩率,横向 cm/cm
@Time 86400 sec
in/in
@Time 24.0 hour
ASTM D955
cm/cm
@Time 86400 sec
in/in
@Time 24.0 hour
ISO 294
机械性能额定值 (公制)额定值 (英制)测试方法
抗张强度(断裂) MPa psi ASTM D638
MPa psi ISO 527
抗张强度(屈服) MPa psi ISO 527
MPa psi ASTM D638
伸长率 (断裂) ASTM D638
ISO 527
屈服伸长率 ISO 527
ASTM D638
拉伸模量 GPa ksi 50 mm/min; ASTM D638
GPa ksi 1 mm/min; ISO 527
弯曲强度 MPa psi ASTM D790
MPa psi ISO 178
弯曲模量 GPa ksi ASTM D790
GPa ksi ISO 178
悬壁梁缺口冲击强度 J/cm ft-lb/in ASTM D256
悬壁梁无缺口冲击强度 ASTM D4812
悬壁梁缺口冲击强度 kJ/m² ft-lb/in² 80*10*4; ISO 180/1A
悬壁梁无缺口冲击强度 kJ/m² ft-lb/in² 80*10*4; ISO 180/1U
落锤总能量 J ft-lb Instrumented Impact Energy @ peak; ASTM D3763
冲击试验 J ft-lb Multiaxial Impact; ISO 6603
动态摩擦系数 ASTM D3702 Modified
静态摩擦系数 ASTM D3702 Modified
K (wear) Factor x 10-8 mm³/N-M x 10-10 in³-min/ft-lb-hr Washer; ASTM D3702 Modified
热性能额定值 (公制)额定值 (英制)测试方法
线形热膨胀系数 - 流动 µm/m-°C
@Temperature -40.0 - 40.0 °C
µin/in-°F
@Temperature -40.0 - 104 °F
ASTM E 831
µm/m-°C
@Temperature -40.0 - 40.0 °C
µin/in-°F
@Temperature -40.0 - 104 °F
ISO 11359-2
线性热膨胀系数,横向流动 µm/m-°C
@Temperature -40.0 - 40.0 °C
µin/in-°F
@Temperature -40.0 - 104 °F
ASTM E 831
µm/m-°C
@Temperature -40.0 - 40.0 °C
µin/in-°F
@Temperature -40.0 - 104 °F
ISO 11359-2
载荷下热变形温度(0.46 MPa) °C
@Thickness 3.20 mm
°F
@Thickness 0.126 in
unannealed; ASTM D648
载荷下热变形温度(1.8 MPa) °C °F Flatw 80*10*4 sp=64mm; ISO 75/Af
°C
@Thickness 3.20 mm
°F
@Thickness 0.126 in
unannealed; ASTM D648
可燃性(UL94)
@Thickness 1.50 mm
@Thickness 0.0591 in
UL 94 by SABIC-IP
Copyright © souwuxing.com All Rights Reserved. 归 搜聚信息科技公司 所有
此数据表中的信息由 搜聚 从该材料的生产商处获得。搜聚 尽最大努力确保此数据的准确性。 但是 搜聚 对这些数据值不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。