| 物理性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 密度 | g/cc | lb/in³ | Average value: 1.18 g/cc Grade Count:142 |
| 吸水率 | Average value: 0.274 % Grade Count:26 | ||
| 饱和吸水率 | Average value: 0.650 % Grade Count:4 | ||
| 粘度 | cP @Temperature 200 - 200 °C | cP @Temperature 392 - 392 °F | Average value: 223000 cP Grade Count:1 |
| cP @Temperature 191 - 191 °C | cP @Temperature 375 - 375 °F | Average value: 223000 cP Grade Count:1 | |
| cP @Shear Rate 3000 - 3000 1/s | cP @Shear Rate 3000 - 3000 1/s | Average value: 223000 cP Grade Count:1 | |
| 线性成型收缩率 | cm/cm | in/in | Average value: 0.00508 cm/cm Grade Count:111 |
| 熔体流动速率 | g/10 min | g/10 min | Average value: 17.1 g/10 min Grade Count:130 |
| 机械性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 洛氏硬度（R 级） | Average value: 101 Grade Count:91 | ||
| 球压硬度 | MPa | psi | Average value: 79.3 MPa Grade Count:7 |
| 极限抗拉强度 | MPa | psi | Average value: 35.7 MPa Grade Count:63 |
| MPa @Temperature 60.0 - 90.0 °C | psi @Temperature 140 - 194 °F | Average value: 11.5 MPa Grade Count:1 | |
| 抗张强度(屈服) | MPa | psi | Average value: 40.4 MPa Grade Count:114 |
| 伸长率 (断裂) | Average value: 15.0 % Grade Count:91 | ||
| @Temperature 60.0 - 90.0 °C | @Temperature 140 - 194 °F | Average value: 72.5 % Grade Count:1 | |
| 屈服伸长率 | Average value: 4.20 % Grade Count:19 | ||
| @Temperature 60.0 - 90.0 °C | @Temperature 140 - 194 °F | Average value: 2.30 % Grade Count:1 | |
| 弹性模量 | GPa | ksi | Average value: 2.24 GPa Grade Count:44 |
| GPa @Temperature 60.0 - 90.0 °C | ksi @Temperature 140 - 194 °F | Average value: 1.70 GPa Grade Count:1 | |
| 弯曲强度 | MPa | psi | Average value: 63.3 MPa Grade Count:108 |
| 弯曲模量 | GPa | ksi | Average value: 2.34 GPa Grade Count:134 |
| 悬壁梁缺口冲击强度 | J/cm | ft-lb/in | Average value: 1.87 J/cm Grade Count:125 |
| J/cm @Temperature -20.0 - 0.000 °C | ft-lb/in @Temperature -4.00 - 32.0 °F | Average value: 1.11 J/cm Grade Count:12 | |
| J/cm @Temperature -40.0 - 0.000 °C | ft-lb/in @Temperature -40.0 - 32.0 °F | Average value: 1.11 J/cm Grade Count:4 | |
| J/cm @Thickness 3.17 - 3.20 mm | ft-lb/in @Thickness 0.125 - 0.126 in | Average value: 1.11 J/cm Grade Count:4 | |
| 悬壁梁无缺口冲击强度 | J/cm | ft-lb/in | Average value: 10.4 J/cm Grade Count:5 |
| 悬壁梁缺口冲击强度 | kJ/m² | ft-lb/in² | Average value: 16.6 kJ/m² Grade Count:18 |
| kJ/m² @Temperature -30.0 - -30.0 °C | ft-lb/in² @Temperature -22.0 - -22.0 °F | Average value: 7.45 kJ/m² Grade Count:8 | |
| 悬壁梁无缺口冲击强度 | kJ/m² - NB | ft-lb/in² - NB | Average value: 70.0 kJ/m² Grade Count:9 |
| kJ/m² @Temperature -30.0 - -30.0 °C | ft-lb/in² @Temperature -22.0 - -22.0 °F | Average value: 47.5 kJ/m² Grade Count:2 | |
| 简支梁无缺口冲击强度 | J/cm² - NB | ft-lb/in² - NB | Average value: 6.17 J/cm² Grade Count:13 |
| J/cm² @Temperature -30.0 - -20.0 °C | ft-lb/in² @Temperature -22.0 - -4.00 °F | Average value: 4.47 J/cm² Grade Count:6 | |
| 简支梁缺口冲击强度 | J/cm² | ft-lb/in² | Average value: 1.62 J/cm² Grade Count:19 |
| J/cm² @Temperature -30.0 - -20.0 °C | ft-lb/in² @Temperature -22.0 - -4.00 °F | Average value: 0.744 J/cm² Grade Count:9 | |
| 加德纳冲击 | J | ft-lb | Average value: 18.2 J Grade Count:4 |
| 电气性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 电阻率 | 1e+05 - ohm-cm | 1e+05 - ohm-cm | Average value: 1.65e+15 ohm-cm Grade Count:27 |
| 表面电阻 | 1e+05 - ohm | 1e+05 - ohm | Average value: 5.86e+14 ohm Grade Count:8 |
| 介电常数 | Average value: 2.89 Grade Count:7 | ||
| 介电强度 | kV/mm | kV/in | Average value: 26.4 kV/mm Grade Count:16 |
| 耗散因数 | Average value: 0.00795 Grade Count:7 | ||
| 耐电弧性 | sec | sec | Average value: 81.4 sec Grade Count:7 |
| 相比耐漏电起痕指数(CTI) | V | V | Average value: 464 V Grade Count:16 |
| 热丝引燃 (HWI) | sec | sec | Average value: 33.6 sec Grade Count:9 |
| 高电弧燃烧，HAI | arcs | arcs | Average value: 134 arcs Grade Count:9 |
| 高压电弧跟踪率，HVTR | mm/min | in/min | Average value: 102 mm/min Grade Count:9 |
| 热性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 线性热膨胀系数 | µm/m-°C | µin/in-°F | Average value: 94.5 µm/m-°C Grade Count:17 |
| 线性热膨胀系数,横向流动 | µm/m-°C | µin/in-°F | Average value: 86.1 µm/m-°C Grade Count:4 |
| 导热系数 | W/m-K | BTU-in/hr-ft²-°F | Average value: 0.187 W/m-K Grade Count:4 |
| Hot Ball Pressure Test | °C | °F | Average value: 95.0 °C Grade Count:5 |
| 载荷下热变形温度(0.46 MPa) | °C | °F | Average value: 89.5 °C Grade Count:55 |
| 载荷下热变形温度(1.8 MPa) | °C | °F | Average value: 87.9 °C Grade Count:119 |
| 维卡软化温度 | °C | °F | Average value: 93.7 °C Grade Count:101 |