| 物理性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 比重 | g/cc | g/cc | ASTM D792 |
| 密度 | g/cc | lb/in³ | ISO 1183 |
| 水分吸收 | 23°C / 50% RH; ISO 62 | ||
| 饱和吸水率 | ISO 62 | ||
| 线性成型收缩率,Flow | cm/cm @Thickness 3.20 mm | in/in @Thickness 0.126 in | SABIC Method |
| 熔体流动速率 | g/10 min @Load 10.0 kg, Temperature 220 °C | g/10 min @Load 22.0 lb, Temperature 428 °F | ASTM D1238 |
| g/10 min @Load 3.80 kg, Temperature 280 °C | g/10 min @Load 8.38 lb, Temperature 536 °F | ASTM D1238 | |
| g/10 min @Load 5.00 kg, Temperature 260 °C | g/10 min @Load 11.0 lb, Temperature 500 °F | ASTM D1238 | |
| Melt Index of Compound | g/10 min @Load 10.0 kg, Temperature 220 °C | g/10 min @Load 22.0 lb, Temperature 428 °F | MVR [cm^3/10 min]; ISO 1133 |
| g/10 min @Load 5.00 kg, Temperature 260 °C | g/10 min @Load 11.0 lb, Temperature 500 °F | MVR [cm^3/10 min]; ISO 1133 |
| 机械性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 洛氏硬度（R 级） | ASTM D785 | ||
| 抗张强度(断裂) | MPa | psi | 50 mm/min; ISO 527 |
| MPa | psi | Type I, 50 mm/min; ASTM D638 | |
| 抗张强度(屈服) | MPa | psi | Type I, 50 mm/min; ASTM D638 |
| MPa | psi | 50 mm/min; ISO 527 | |
| 伸长率 (断裂) | 50 mm/min; ISO 527 | ||
| Type I, 50 mm/min; ASTM D638 | |||
| 屈服伸长率 | 50 mm/min; ISO 527 | ||
| Type I, 50 mm/min; ASTM D638 | |||
| 拉伸模量 | GPa | ksi | 5 mm/min; ASTM D638 |
| GPa | ksi | 1 mm/min; ISO 527 | |
| GPa | ksi | 50 mm/min; ASTM D638 | |
| 弯曲强度 | MPa | psi | 2 mm/min; ISO 178 |
| MPa | psi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| 弯曲模量 | GPa | ksi | 2 mm/min; ISO 178 |
| GPa | ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| 悬壁梁缺口冲击强度 | J/cm | ft-lb/in | ASTM D256 |
| J/cm @Temperature -30.0 °C | ft-lb/in @Temperature -22.0 °F | ASTM D256 | |
| kJ/m² | ft-lb/in² | 80*10*4; ISO 180/1A | |
| kJ/m² @Temperature -30.0 °C | ft-lb/in² @Temperature -22.0 °F | 80*10*4; ISO 180/1A | |
| 简支梁缺口冲击强度 | J/cm² | ft-lb/in² | Edgew 80*10*4 sp=62mm; ISO 179/1eA |
| Dart Drop, Total Energy | J @Temperature -30.0 °C | ft-lb @Temperature -22.0 °F | ASTM D3763 |
| J @Temperature 23.0 °C | ft-lb @Temperature 73.4 °F | ASTM D3763 |
| 电气性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 耗散因数 | @Frequency 100000 Hz | @Frequency 100000 Hz | ASTM D150 |
| @Frequency 1.00e+6 Hz | @Frequency 1.00e+6 Hz | ASTM D150 | |
| 相比耐漏电起痕指数(CTI) | V | V | IEC 60112 |
| 热性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 线形热膨胀系数 - 流动 | µm/m-°C @Temperature -40.0 - 40.0 °C | µin/in-°F @Temperature -40.0 - 104 °F | ASTM E 831 |
| µm/m-°C @Temperature -40.0 - 40.0 °C | µin/in-°F @Temperature -40.0 - 104 °F | ISO 11359-2 | |
| 线性热膨胀系数,横向流动 | µm/m-°C @Temperature -40.0 - 40.0 °C | µin/in-°F @Temperature -40.0 - 104 °F | ASTM E 831 |
| µm/m-°C @Temperature -40.0 - 40.0 °C | µin/in-°F @Temperature -40.0 - 104 °F | ISO 11359-2 | |
| Hot Ball Pressure Test | <= °C | <= °F | IEC 60695-10-2 |
| 载荷下热变形温度(0.46 MPa) | °C | °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| °C @Thickness 3.20 mm | °F @Thickness 0.126 in | unannealed; ASTM D648 | |
| 载荷下热变形温度(1.8 MPa) | °C | °F | Edgew 120*10*4 sp=100mm; ISO 75/Ae |
| °C | °F | Flatw 80*10*4 sp=64mm; ISO 75/Af | |
| °C @Thickness 3.20 mm | °F @Thickness 0.126 in | unannealed; ASTM D648 | |
| 维卡软化温度 | °C | °F | Rate B/50; ASTM D1525 |
| °C | °F | Rate B/50; ISO 306 | |
| °C | °F | Rate B/120; ISO 306 | |
| 可燃性(UL94) | @Thickness 1.50 mm | @Thickness 0.0591 in | UL 94 |
| 光学性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 光泽度 | untextured, 60 degrees; ASTM D523 |
| 材料描述 | 测试方法 | |
|---|---|---|
| UV-light, water exposure/immersion | F1 | UL 746C |