Features: Good Chemical Resistance; Good Creep Resistance; Good Dimensional Stability; Good Stiffness; High Heat Resistance; High Stiffness; High Strength; High Temperature Strength; Low Moisture Absorption
Uses: Automotive Electronics; Connectors; Electrical Parts; Electrical/Electronic Applications
Injection Molding Notes: Amodel® compounds are shipped in moisture-resistant packages at moisture levels according to specifications. Sealed, undamaged bags should be preferably stored in a dry room at a maximum temperature of 50°C (122°F) and should be protected from possible damage. If only a portion of a package is used, the remaining material should be transferred into a sealable container. It is recommended that Amodel® resins be dried prior to molding.
Information provided by Solvay Specialty Polymers.| 物理性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 密度 | g/cc | lb/in³ | Dry; ISO 1183 |
| 填料含量 | Glass Fiber | ||
| 线性成型收缩率,Flow | cm/cm | in/in | Dry |
| 线性成型收缩率，横向 | cm/cm | in/in | Dry; ASTM D955 |
| 电气性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 体积电阻率 | ohm-cm | ohm-cm | ASTM D257 |
| 介电常数 | @Frequency 1.00e+6 Hz | @Frequency 1.00e+6 Hz | ASTM D150 |
| @Frequency 60.0 Hz | @Frequency 60.0 Hz | ASTM D150 | |
| 介电强度 | kV/mm @Thickness 3.20 mm | kV/in @Thickness 0.126 in | ASTM D149 |
| 耗散因数 | @Frequency 1.00e+6 Hz | @Frequency 1.00e+6 Hz | ASTM D150 |
| @Frequency 60.0 Hz | @Frequency 60.0 Hz | ASTM D150 | |
| 相比耐漏电起痕指数(CTI) | V | V | UL 746 |
| 高压电弧跟踪率，HVTR | mm/min | in/min | UL 746 |
| 加工性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 料筒后部温度 | °C | °F | |
| 料筒中部温度 | °C | °F | |
| 料筒前部温度 | °C | °F | |
| 加工（熔体）温度 | °C | °F | |
| 模具温度 | °C | °F | |
| 干燥温度 | °C @Time 14400 sec | °F @Time 4.00 hour | |
| 水分含量 | Suggested Max |
| 材料描述 | 测试方法 | |
|---|---|---|
| 可用性 | Africa & Middle East | |
| Asia Pacific | ||
| Europe | ||
| Latin America | ||
| North America | ||
| 颜色 | Black; Natural | |
| 形式 | Pellets | |
| 加工技术 | Injection Molding |