YUCLAIR® FV149M

线性低密度聚乙烯

SK Global Chemical

产品说明:

YUCLAIR FV149M is butene-1 copolymer designed for use in general purpose film application.
YUCLAIR FV149M provides stronger film than ones made from competitive LLDPE film grades. Therefore YUCLAIR FV149M shows superior tensile strength, tear strength, gel-free, antiblock and sealibility. Outstanding clarity and good processibility make this resin an ideal choice for film application when blended with conventional LDPE.
YUCLAIR FV149M can be processed readily into blown film using standard extrusion techniques.
YUCLAIR FV149M complies with FDA regulations in 21 CFR177.1520 for all food contact.
YUCLAIR® FV149M 物性表
基本信息
添加剂
  • 抗结块剂
  • 增滑剂
特性
  • 高拉伸强度
  • 共聚物
  • 光滑性
  • 抗结块性
  • 可加工性,良好
  • 良好的撕裂强度
  • 清晰度,高
  • 食品接触的合规性
用途
  • 薄膜
  • 混合
  • 通用
机构评级
  • FDA 21 CFR 177.1520
加工方法
  • 吹塑薄膜
  • 挤出
物理性能额定值单位制测试方法
密度 g/cm³ASTM D1505
熔流率(熔体流动速率) (190°C/2.16 kg)g/10 minASTM D1238
薄膜额定值单位制测试方法
薄膜厚度 - 经测试 µmASTM D746
抗张强度 ASTM D882
    MD : 屈服, 20 µm MPaASTM D882
    TD : 屈服, 50 µm MPaASTM D882
    MD : 断裂, 50 µm MPaASTM D882
    TD : 断裂, 50 µm MPaASTM D882
伸长率 ASTM D882
    MD : 断裂, 50 µm %ASTM D882
    TD : 断裂, 50 µm %ASTM D882
Spencer Impact (50.0 µm) JASTM D3420
补充信息额定值单位制测试方法
Tear Strength ASTM D1922
    MD : 50.0 µm kN/mASTM D1922
    TD : 50.0 µm kN/mASTM D1922
热性能额定值单位制测试方法
脆化温度 °CASTM D746
维卡软化温度 °CASTM D1525
光学性能额定值单位制测试方法
雾度 (50.0 µm)%ASTM D1003
挤出额定值单位制
料筒1区温度 °C
料筒3区温度 °C
料筒5区温度 °C
口模温度 °C
挤压说明
Film Extrusion Condition: Screw dia 50, Die dia 150, BUR 2.2Die gap 1.8, Screw RPM 45, L/S 7.2