- LEXAN™ 143R resin物性表
LEXAN™ 143R resin
PC
SABIC Innovative Plastics
产品说明
UL rated HB as of 10/97. 200 series recommended when V-2 rating required. Nonhalogenated. 10.5 MFR. UV-stabilized. Internal mold release.
搜物性提供30万余种物性表数据,如要查看关于
LEXAN™ 143R resin 完整物性数据,以及其替代物,黄卡信息,下载物性表PDF.
请 获得完整功能体验。
基本信息 | |
---|
黄卡编号 | |
添加剂 | |
特性 | |
加工方法 | |
多点数据 | - Coefficient of Thermal Expansion vs. Temperature (ASTM E831)
- Flexural DMA (ASTM D4065)
- Pressure-Volume-Temperature (PVT - Zoller Method)
- Shear DMA (ASTM D4065)
- Tensile Fatigue
- Tensile Stress vs. Strain (ASTM D638)
- Thermal Conductivity vs. Temperature (ASTM E1530)
- Viscosity vs. Shear Rate (ASTM D3835)
|
物理性能 | 额定值 | 单位制 | 测试方法 |
---|
比重 | | | ASTM D792 |
-- | | g/cm³ | ASTM D792 |
-- | | g/cm³ | ASTM D792 |
特定体积 | | cm³/g | ASTM D792 |
熔流率(熔体流动速率) (300°C/1.2 kg) | | g/10 min | ASTM D1238 |
收缩率 -
流动 (3.20 mm) | | % | 内部方法 |
吸水率 | | | ASTM D570 |
24 hr | | % | ASTM D570 |
平衡, 23°C | | % | ASTM D570 |
平衡, 100°C | | % | ASTM D570 |
室外适用性 | | | UL 746C |
硬度 | 额定值 | 单位制 | 测试方法 |
---|
洛氏硬度 | | | ASTM D785 |
M 级 | | | ASTM D785 |
R 级 | | | ASTM D785 |
机械性能 | 额定值 | 单位制 | 测试方法 |
---|
抗张强度 1 | | | ASTM D638 |
屈服 | | MPa | ASTM D638 |
断裂 | | MPa | ASTM D638 |
伸长率 2 | | | ASTM D638 |
屈服 | | % | ASTM D638 |
断裂 | | % | ASTM D638 |
弯曲模量 3(50.0 mm 跨距) | | MPa | ASTM D790 |
弯曲强度 4(屈服, 50.0 mm 跨距) | | MPa | ASTM D790 |
泰伯耐磨性 (1000 Cycles, 1000 g, CS-17 转轮) | | mg | ASTM D1044 |
冲击性能 | 额定值 | 单位制 | 测试方法 |
---|
悬壁梁缺口冲击强度 (23°C) | | J/m | ASTM D256 |
无缺口悬臂梁冲击 (23°C) | | J/m | ASTM D4812 |
落锤冲击 (23°C) | | J | ASTM D3029 |
拉伸冲击强度 5 | | kJ/m² | ASTM D1822 |
热性能 | 额定值 | 单位制 | 测试方法 |
---|
载荷下热变形温度 | | | ASTM D648 |
0.45 MPa, 未退火, 6.40 mm | | °C | ASTM D648 |
1.8 MPa, 未退火, 6.40 mm | | °C | ASTM D648 |
维卡软化温度 | | °C | ASTM D1525 6 |
线形热膨胀系数 -
流动 (-40 到 95°C) | | cm/cm/°C | ASTM E831 |
比热 | | J/kg/°C | ASTM C351 |
导热系数 | | W/m/K | ASTM C177 |
RTI Elec | | °C | UL 746 |
RTI Imp | | °C | UL 746 |
RTI | | °C | UL 746 |
电气性能 | 额定值 | 单位制 | 测试方法 |
---|
体积电阻率 | | ohms·cm | ASTM D257 |
介电强度 (3.20 mm, in Air) | | kV/mm | ASTM D149 |
介电常数 | | | ASTM D150 |
50 Hz | | | ASTM D150 |
60 Hz | | | ASTM D150 |
1 MHz | | | ASTM D150 |
耗散因数 | | | ASTM D150 |
50 Hz | | | ASTM D150 |
60 Hz | | | ASTM D150 |
1 MHz | | | ASTM D150 |
相比耐漏电起痕指数(CTI) | | | UL 746 |
高电弧燃烧指数(HAI) | | | UL 746 |
高电压电弧起痕速率 (HVTR) | | | UL 746 |
热丝引燃 (HWI) | | | UL 746 |
可燃性 | 额定值 | 单位制 | 测试方法 |
---|
UL 阻燃等级 (0.762 mm) | | | UL 94 |
极限氧指数 | | % | ASTM D2863 |
光学性能 | 额定值 | 单位制 | 测试方法 |
---|
折射率 | | | ASTM D542 |
透射率 (2540 µm) | | % | ASTM D1003 |
雾度 (2540 µm) | | % | ASTM D1003 |
注射 | 额定值 | 单位制 | |
---|
干燥温度 | | °C | |
干燥时间 | | hr | |
干燥时间,最大 | | hr | |
建议的最大水分含量 | | % | |
建议注射量 | | % | |
料筒后部温度 | | °C | |
料筒中部温度 | | °C | |
料筒前部温度 | | °C | |
射嘴温度 | | °C | |
加工(熔体)温度 | | °C | |
模具温度 | | °C | |
背压 | | MPa | |
螺杆转速 | | rpm | |
排气孔深度 | | mm | |
备注 |
---|
1 . | 类型 1, 50 mm/min |
2 . | 类型 1, 50 mm/min |
3 . | 1.3 mm/min |
4 . | 1.3 mm/min |
5 . | Type S |
6 . | 标准 B (120°C/h), 载荷2 (50N) |