| Plastication: 50rpmInjection Time: 2 to 8 secHold Time: 1 to 5 sec/mmCure Time, 0.125 in: 5 to 12 sec/mmAll ISO properties listed were tested in accordance with ISO 3167The value listed as Molding Shrinkage, ISO 294-4, was tested in accordance with ISO 2577.ISO Type: PF 2 C3Powder Density, ISO 60: 0.6 to 0.75 g/cm³Post Shrinkage, ISO 2577: 0.1 to 0.2%HDT A (1.80 MPa) Unannealed, ISO 75A, Injection Molding: 170 to 190°CHDT A (8.0 MPa) Unannealed, ISO 75A, Injection Molding: 150 to 170°CCLTE, Flow (TMA), ASTM E831, Injection Molding: 20 to 30 cm^-6/cm°CCLTE, Transverse (TMA), ASTM E831, Injection Molding: 30 to 40 cm^-6/cm°CFlexural Strength, ISO 178, Injection Molding: 140 to 160 MPaFlexural Modulus, ISO 178, Injection Molding: 7.5 to 9 GPaStrain to failure in Flexure, ISO 178, Injection Molding: 1.6 to 1.8%Tensile Stress at Break, ISO 527-1,-2, Injection Molding: 65 to 75 MPaTensile Modulus, ISO 527-1,-2, Injection Molding: 9.5 to 11.5 GPaTensile Strain at Break, ISO 527-1,-2, Injection Molding: 1.05 to 1.15%Charpy Notched Impact Strength, ISO 179, Injection Molding: 4.5 to 5.5 kJ/m²Charpy Unnotched Impact Strength, ISO 179, Injection Molding: 13 to 15 kJ/m²Compressive Strength, ISO 604: 190 to 220 MPaInsulation Resistance dry, IEC 167: 1e10 to 1e12 ohm |